Configuration description of the hottest flexo ink

2022-08-08
  • Detail

Configuration description of flexographic ink

from the current application situation, when the load of the force measuring machine is close to 50kN, its printing matrix can be divided into two types, namely, porous matrix and non porous matrix. Water based flexographic ink is generally used for printing on the surface of porous substrate; Solvent based inks are used for about two-thirds of the printing on the surface of non porous substrates. The use of water-based flexographic ink at home and abroad is an increasing trend

1. Type: as mentioned above, flexo ink is a liquid ink, and its drying method is to penetrate into the matrix (paper) or volatilize the solvent

2. Preparation method: the solvent used in this low viscosity (CPS) liquid ink is based on dissolving the polymer in the ink. The typical solvents used are water and alcohol, as well as a small amount of ethylene glycol ether, monobasic and aliphatic hydrocarbons. Its film-forming polymers are polyphthalamide, nitrocellulose, rosin, lac and acrylic vinegar - usually one of these polymers is used to modify the other (for example, nitrocellulose can increase heat resistance; polyphthalamide can increase gloss and flexibility). In most flexographic inks, more than two kinds of polymers or solvents are generally used to get the sense of well-being of thousands of families in terms of performance. When we finish the experiment, we will settle the balance of the workbench. Flexographic ink system generally contains 7-15 different components, which constitute the total components of pigments, polymers, solvents and additives used in typical flexographic ink

the following is a brief description of the preparation of solvent based ink and water-based flexographic ink:

1 Solvent based flexographic ink: as mentioned above, solvent based flexographic ink is mainly prepared to print non porous substrate surfaces

about 75% of plastic inks use alcohol soluble polyamide resin, and its representative reference formula is as follows:

component weight% polyamide resin 13s/s nitrocellulose 2* organic pigment 15 filler 5 plasticizer, wax 5 ethanol 55 ester 5100

note: * if white ink based on TiO2: is manufactured, this amount can be doubled and the amount of ethanol can be reduced

the following reference formula is modified nitrocellulose ink, which has good gloss and heat resistance, and is suitable for printing foil, coated cellophane and paper:

component weight% polyphthalamine resin 10s/s nitrocellulose 5* organic pigment 15 filler 5 plasticizer, wax 10 ethanol 50 ester 5100 if you need to print ink for coated cellophane, you should replace the film-forming agent in the above formula, namely modified rosin, with acrylic resin, Only in this way can the heat seal not be affected

at present, flexible plastic film for composite packaging is developing rapidly, which requires an ink, that is, composite ink is suitable for printing this plastic film, and then compounded with another plastic film or paper to make sealed packaging with good printing and heat sealing performance. The composite ink used for printing here does not contact the inner packaging or the air. This kind of composite ink does not need gloss, nor does it need to have resistance to scratches and friction (because they are protected by the composite film). This kind of ink contains no wax or very little, so it will not reduce the adhesion between composite films